Local structure analysis of Re/Fe2O3 catalysts by high energy XAFS
問い合わせ番号
SOL-0000001205
ビームライン
BL01B1（XAFS I）
学術利用キーワード
| A. 試料 | 無機材料 |
|---|---|
| B. 試料詳細 | 非晶質、ガラス |
| C. 手法 | 吸収、及びその二次過程 |
| D. 手法の詳細 | XAFS, EXAFS, XANES |
| E. 付加的測定条件 | 偏光（直線）, 低温（〜液体ヘリウム） |
| F. エネルギー領域 | Ｘ線（>40 keV） |
| G. 目的・欲しい情報 | 化学状態, 結合状態, 局所構造, 機能構造相関, 機能発現 |
産業利用キーワード
| 階層1 | ディスプレイ, 環境, 化学製品, その他 |
|---|---|
| 階層2 | 触媒, 環境物質 |
| 階層3 | |
| 階層4 | 局所構造, 化学状態 |
| 階層5 | XAFS, NEXAFS |
分類
A80.34 触媒化学, M40.10 XAFS
利用事例本文
In this solution, EXAFS method was applied to study local environments of Re(9.2 wt%)/Fe2O3, catalysts for methanol partial oxidation reaction to produce methylal. The EXAFS method is a powerful technique to study local structure (distance, coordination number, species of neighbor atoms) of selected elements both in crystalline states and in non-crystalline states. For this sample, Re L3-edge EXAFS is difficult to measure due to large absorption by Fe2O3 support. High quality EXAFS spectrum could be measured at high energy Re K-edge (Fig. 1). EXAFS analysis revealed that Re and Fe atoms form a Re-Fe binary oxide and stabilize an active ReO4 structure (Fig. 2).
Fig. 1 Re K-edge EXAFS spectrum of Re(9.2 wt%)/Fe2O3.
Fig. 2 Proposed structure oｆ Re active site on Re/Fe2O3.
画像ファイルの出典
所内報
誌名
SPring-8 Research Frontiers, 2000-2001
ページ
53,54
測定手法
XAFS spectra of dense samples are taken in a transmission mode. This method is performed by measuring x-ray absorption as a function of x-ray energy around an absorption edge of a selected element. Since EXAFS oscillation is smeared in high-energy region, XAFS spectra at more than 50 keV are usually measured at low temperature (10 K) to get high quality data by lowering temperature factor. Acquisition time per XAFS spectrum using QXAFS mode is 30-45 min in this solution.
画像ファイルの出典
図なし
測定準備に必要なおおよその時間
2 時間
測定装置
| 装置名 | 目的 | 性能 |
|---|---|---|
| XAFS Measurement System | Measurement of XAFS spectra | 3.8-113 keV |
| Ionization Chamber | Measurement of transmission mode XAFS | concentration > 1000 ppm |
参考文献
| 文献名 |
|---|
| T. Shido et al., SPring-8 Reserch Frontiers, 2000-2001, (2001) 53 |
関連する手法
アンケート
SPring-8だからできた測定。他の施設では不可能もしくは難しい
本ビームラインの主力装置を使っている
測定の難易度
初心者でもOK
データ解析の難易度
中程度
図に示した全てのデータを取るのにかかったシフト数
1シフト以下